参数资料
| 型号： | 3-5-4905 |
| 厂商： | 3M (TC) |
| 文件页数： | 9/11页 |
| 文件大小： | 0K |
| 描述： | TAPE VHB CLEAR 3" GEN PURPOSE |
| 产品培训模块： | VHB™ Tape |
| 视频文件： | 3M VHB adhesive demonstration - Another Geek Moment |
| MSDS 材料安全数据表： | 49zz MSDS |
| 标准包装： | 1 |
| 系列： | VHB™ 4905 |
| 胶带类型： | 双涂层，双面 |
| 胶合剂： | 丙烯酸 |
| 背衬，载体： | 聚乙烯薄膜 |
| 厚度： | 0.020"（20 mils，0.508mm） |
| 厚度 - 胶合剂： | 0.0150"（15.0 mils，0.381mm） |
| 厚度 - 背胶，载体，衬垫： | 0.0050"（5.0 mils，0.127mm） |
| 宽： | 3.00"（76.20mm）1/4' |
| 长度： | 15'（4.6m）5 码 |
| 颜色： | 透明 |
| 使用： | 通用 |
| 温度范围： | 200°F（93°C） |
| 包装： | 散装 |
| 其它名称： | 3M10163 |
3M ? VHB ? Tapes
Application Techniques
Clean: Most substrates are best prepared by cleaning with a 50:50 mixture of isopropyl alcohol (IPA*) and
water prior to applying 3M? VHB? Tapes.
Exceptions to the general procedure that may require additional surface preparation include:
? Heavy Oils: A degreaser or solvent-based cleaner may be required to remove heavy oil or grease from a
surface and should be followed by cleaning with IPA/water.
? Abrasion: Abrading a surface, followed by cleaning with IPA/water, can remove heavy dirt or oxidation
and can increase surface area to improve adhesion.
? Adhesion Promoters: Priming a surface can significantly improve initial and ultimate adhesion to many
materials such as plastics and paints.
? Porous surfaces: Most porous and fibered materials such as wood, particleboard, concrete, etc. need to be
sealed to provide a unified surface.
? Unique Materials: Special surface preparation may be needed for glass and glass-like materials, copper
and copper containing metals, and plastics or rubber that contain components that migrate (e.g. plasticizers).
Refer to 3M Technical Bulletin “Surface Preparation for 3M? VHB? Tape Applications” for additional
details and suggestions. (70-0704-8701-5)
*Note: These cleaner solutions contain greater than 250 g/l of volatile organic compounds (VOC). Please
consult your local Air Quality Regulations to be sure the cleaner is compliant. When using solvents,
be sure to follow the manufacturer ’s precautions and directions for use when handling such materials.
Pressure: Bond strength is dependent upon the amount of adhesive-to-surface contact developed. Firm
application pressure develops better adhesive contact and helps improve bond strength. Typically, good surface
contact can be attained by applying enough pressure to insure that the tape experiences approximately 15 psi
(100 kPa) pressure. Either roller or platen pressure can be used. Note that rigid surfaces may require 2 or 3 times
that much pressure to make the tape experience 15 psi.
Temperature: Ideal application temperature range is 70°F to 100°F (21°C to 38°C). Pressure sensitive
adhesives use viscous flow to achieve substrate contact area. Minimum suggested application temperatures:
? 50°F (10°C): 3M? VHB? Tapes 4950, 5952, 4910, 4952, 4611, 4622 families.
? 60°F (15°C): 3M? VHB? Tapes 4941, 4945 families.
? 32°F (0°C): 3M? VHB? Tape 4951 families.
Note: Initial tape application to surfaces at temperatures below these suggested minimums is not
recommended because the adhesive becomes too firm to adhere readily. However, once properly
applied, low temperature holding is generally satisfactory.
To obtain good performance with all 3M? VHB? Tapes, it is important to ensure that the surfaces are dry
and free of condensed moisture.
Time: After application, the bond strength will increase as
Bond Typical Build vs. Time
●
★
★
●
●
the adhesive flows onto the surface (also referred to as “wet out”).
At room temperature approximately 50% of ultimate bond
strength will be achieved after 20 minutes, 90% after 24 hours
and 100% after 72 hours. This flow is faster at higher temperatures
and slower at lower temperatures. Ultimate bond strength can be
achieved more quickly (and in some cases bond strength can be
increased) by exposure of the bond to elevated temperatures
60
20
PERCENT OF FULL BOND
100 ■ ■ ■
■ ●
●
80 ■ ●
●
●
★
40 ★
★
■
●
★
■
●
★
■
●
■
★
■
★
■
★
●
■ ●
★
●
★
●
★
(e.g. 150°F [66°C] for 1 hour). This can provide better adhesive
wetout onto the substrates. Abrasion of the surfaces or the use of
0
20 MIN
1 HOUR 24 HOURS
● ROOM TEMP ★ 50°F
■ 150°F or ABRADE
72 HOURS
primers/ adhesion promoters can also have the effect of increasing
bond strength and achieving ultimate bond strength more quickly.
-9-
相关PDF资料 |
PDF描述 |
|---|---|
| 0395332410 | 5.08MM EURO PLUG STR BLK 10POS |
| 2-5-4941 | TAPE VHB ACRYLIC FOAM 2" X 5YD |
| 0395332310 | 5.08MM EURO PLUG STR BLK 10POS |
| 0395329511 | 5.08MM EURO HEADER RA GRN 11POS |
| LAA108P | RELAY OPTOMOS 300MA DP-NO 8FLTPK |
相关代理商/技术参数 |
参数描述 |
|---|---|
| 35-4905 | 制造商:MCM 功能描述:HEADSET MIC + VOLUME CONTROL |
| 354905-1 | 功能描述:剥线和切削工具 SHEAR PLATE REAR RoHS:否 制造商:Molex 产品:Cable Strippers 类型: 描述/功能:Stripper |
| 354905GY | 制造商:Littelfuse 功能描述:Fuse Block 30A 300V Quick Connect Screw Mount |
| 354905-GY | 制造商:LITTELFUSE 制造商全称:Littelfuse 功能描述:Fuse Blocks and Clips |
| 354906-1 | 功能描述:SHEAR HOLDER 制造商:te connectivity amp connectors 系列:* 零件状态:有效 标准包装:1 |
发布紧急采购，3分钟左右您将得到回复。